- Catalytic Grade Titanium Dioxide with ungsten
- Titanium Tungsten Silicon Powder
Quick Details
- ProName: Catalytic Grade Titanium Dioxide with ...
- CasNo: 1317-80-2
- Molecular Formula: O2Ti + W
- Application: SCR denitration catalyst
- DeliveryTime: immediate from stock
- PackAge: 25kg/drum
- Port: Shanghai
- ProductionCapacity: 3
- Purity: 99%min
- Storage: Store in dry, dark place
- Transportation: by sea / air
- LimitNum: 0 Metric Ton
- Product Ecification: 99%MIN
- Grade: first grade
- Brand: CSR
Superiority
SkyRun Industrial CO.,LTD is a leading chemical producer in China. We supply Intermediate, Agro-Chemical and Petrol Chemicals for different usage.SkyRun Industrial CO.,LTD is a leading chemical producer in China. We supply Intermediate, Agro-Chemical and Petrol Chemicals for different usage.
Their are two production bases in China: Jiangsu and Gansu. Our research center located in Hanghou city . You are always welcome for plant audit, We assure you by offering qualified material and Professional services
For more information on SKYRUN products and services, please contact us by email
Details
Quality performance
Technical index |
Titanium Tungsten Powder for Catalyst |
Titanium Tungsten Silicon Powder |
Titanium Dioxide for Catalyst |
Titanium Silicon Powder |
|
BET surface |
m2/g |
90±10 |
105±10 |
90±10 |
105±10 |
Grain size |
nm |
10-20 |
10-20 |
10-20 |
10-20 |
Aggregate size D50 |
um |
1.1±0.3 |
1.1±0.3 |
1.1±0.3 |
1.1±0.3 |
Rutile content% |
≤ |
0.5 |
0.5 |
0.5 |
0.5 |
PH (10% water suspension) |
1.2-3.0 |
1.2-3.0 |
1.2-3.0 |
1.2-3.0 |
|
Calcination of weightlessness% |
≤ |
5.0 |
5.0 |
5.0 |
5.0 |
TiO2 Content% |
≥ |
90 |
85 |
90 |
90 |
SO42-Content% |
1.5-3.5 |
1.5-3.5 |
1.5-3.5 |
1.5-3.5 |
|
Fe2O3 Content ppm |
≤ |
100 |
100 |
100 |
100 |
K2O Content ppm |
≤ |
100 |
100 |
100 |
100 |
Na2O Content ppm |
≤ |
100 |
100 |
100 |
100 |
WO3Content % |
5.0±0.7 |
5.0±0.7 |
- |
- |
|
SiO2 Content % |
- |
5.0±0.7 |
- |
5.0±0.7 |
|
Volatile(105℃) % |
≤ |
2.0 |
2.0 |
2.0 |
2.0 |